R-BLUE

Xylan coated T-bolts and nuts.
Manufactured in the USA.

LOW FRICTION Reduces make up torque as much as 70%.
EXCEPTIONAL CORROSION RESISTANCE Xylan 1424 with Zinc Plating base coat survives salt fog testing (ASTM B117) for up to 3,000 hours.

RESISTANT TO ABRASION, WEAR & CHIPPING Achieves a 5A rating for adhesion per ASTM D3359.

 
 

MATERIALS

T-BOLT High Strength, Low-Alloy / Corrosion Resistant Steel, (Cor-Ten™), (Mayari-R™). Meets or exceeds ASTM A 588, Grade E. AWWA C111 composition specifications. The material specifications of ASTM A-588 meets or exceeds ASTM A 307 Grade A. 
NUT High strength, low-alloy / corrosion resistant steel, (Cor-Ten™), (Mayari-R™). Meets or exceeds ASTM A563 Grade, C3, AWWA C111 composition specifications. The material specifications of ASTM A 563 Grade C3 meets or exceeds ASTM A 563 Grade A.
COATING Xylan 1424 polytetrafluoroethylene (PTFE) a dry-film lubricant (VOC compliant), resin bonded, PTFE based coating formulated for use on fasteners to prevent corrosion and facilitate make up torque.
BASE COAT Zinc plating.

 